| FITTING AND FLANGE MECHANICAL PROPERTIES | ||||
| Material |
Tensil Strength (K. g./mm2 ) |
Yield Strength (K. g./mm2 ) |
Elongation (%) |
Area REduction (%) |
| A. 182F-304 |
52.8 min. |
21.1 min. |
30 min. |
50 min. |
| A. 182F-304L |
49.3 min. |
17.6 min. |
30 min. |
50 min. |
| A. 182F-316 |
52.8 min. |
21.1 min. |
30 min. |
50 min. |
| A. 182F-316L |
49.3 min. |
17.6 min. |
30 min. |
50 min. |
| FITTING AND FLANGE CHEMICAL COMPOSITION (%) | |||||||||
| C | Mn | Si | S | P | Cr | Ni | Mo | N2 | |
| A.182F-304 |
0.08 max. |
2.0 max. |
1.0 max. |
0.030 max. |
0.040 max. |
18.0-20.0 | 8.0-11.0 | - |
0.10 max. |
| A.182F-304L |
0.035 max. |
2.0 max. |
1.0 max. |
0.030 max. |
0.040 max. |
18.0-20.0 | 8.0-11.0 | - |
0.10 max. |
| A. 182F-316 |
0.08 max. |
2.0 max. |
1.0 max. |
0.030 max. |
0.040 max. |
16.0-18.0 | 10.0-14.0 | 2.0-3.0 |
0.10 max. |
| A.182F-316L |
0.035 max. |
2.0 max. |
1.0 max. |
0.030 max. |
0.040 max. |
16.0-18.0 | 10.0-15.0 | 2.0-3.0 |
0.10 max. |